The effect of gamma irradiation on space charge behaviour and dielectric spectroscopy of low-density polyethylene

Fu, M., Chen, G., Dissado, L. A., Fothergill, J. & Zou, C. (2007). The effect of gamma irradiation on space charge behaviour and dielectric spectroscopy of low-density polyethylene. Paper presented at the 2007 IEEE International Conference on Solid Dielectrics.

[img]
Preview
PDF
Download (196kB) | Preview

Abstract

The influence of gamma irradiation on low-density polyethylene (LDPE) has been studied through space charge measurement and dielectric spectroscopy. Commercial LDPE film with a thickness of 100μm was irradiated with γ-rays at a dose rate of approximately 10kGy/h to different doses up to 100kGy in an atmosphere of air, vacuum and nitrogen respectively. Space charge profiles vary depending on irradiation environments and radiation dose. The space charge profile of a sample after irradiation at 100kGy in air is more complicated than those irradiated in vacuum and nitrogen at same dose. More importantly, the space charge decay rate for the irradiated samples is slower than that of the virgin sample, indicating that the irradiation had changed the material by the generation of deep traps for space charge. Irradiation in air also produced changes in the dielectric spectrum in the frequency range between 10-3Hz and 106Hz where the imaginary part of the permittivity was found to be about one order of magnitude higher than that of the virgin sample (~10-4). This was attributed to oxidation as samples with the same (or lower) radiation dose in vacuum or nitrogen showed no pronounced difference to that of virgin samples.

Item Type: Conference or Workshop Item (Paper)
Additional Information: © 2007 IEEE. Personal use of this material is permitted. Permission from IEEE must be obtained for all other uses, in any current or future media, including reprinting/republishing this material for advertising or promotional purposes, creating new collective works, for resale or redistribution to servers or lists, or reuse of any copyrighted component of this work in other works.
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Divisions: Vice-Chancellor's Portfolio
URI: http://openaccess.city.ac.uk/id/eprint/1364

Actions (login required)

View Item View Item

Downloads

Downloads per month over past year

View more statistics