This paper aims to present the determination of the creep behaviour of a globular microstructure aluminium 7075 alloy semi-solid metal feedstock billets under a constant temperature of 250 °C. Globular microstructures are often preferred in thixoforming processes due to their unique properties and favourable mechanical and high-temperature applications. Less attention has been given to globular microstructure even though the contribution of microstructure to creep behaviour is essential. Therefore, for this test, globular microstructure aluminium 7075 alloy feedstock billets were produced by the direct thermal method. The creep tests were conducted at different stress ranges from 30 to 70 MPa, and the effect of globular microstructure was examined. The results showed that the globular microstructure had the least deformation and the lowest creep rate at a longer deformation time. The fracture surface of the samples was then analysed with scanning electron microscopy (SEM). The microstructural changes that occurred during the test were investigated. SEM analysis revealed that the globular microstructure of the feedstock billet exhibits fewer voids and defects due to a uniform microstructure. The strain exponent value of globular microstructure billets was found to be at n = 4.6 in the stress range between 30 and 70 MPa at a constant temperature. This study is expected to provide an understanding of the creep behaviour of globular microstructures at high temperatures and high-stress conditions.

Publication Type:	Article
Additional Information:	The version of record of this article, first published in Journal of Failure Analysis and Prevention, is available online at Publisher’s website: https://doi.org/10.1007/s11668-024-01917-7
Publisher Keywords:	Aluminium 7075 alloy, Globular microstructure, Feedstock billets, Creep behaviour, Creep strain, Strain exponent
Subjects:	T Technology > TA Engineering (General). Civil engineering (General) T Technology > TJ Mechanical engineering and machinery
Departments:	School of Science & Technology School of Science & Technology > Engineering
SWORD Depositor:	Symplectic Administrator

Export

Downloads